Bainitik issiqlikka chidamli po'lat quvur nima?
Beynit po'latdan matritsaning metallografik tuzilishi foydalanish holatida beynitdir. Uning kimyoviy tarkibi past uglerodli va past qotishma elementlardan iborat, uglerod tarkibi odatda<0.05%, and the main alloying elements are Mn, Cr, Ni, Mo, B, etc. Bainite structure is usually obtained by air cooling or controlling the cooling rate. This type of steel has high strength (530~1500MPa), high toughness, and the tensile strength increases with the decrease of bainite transformation temperature. The process performance (weldability and formability) is good. It is widely used in aviation, ships, boilers, petrochemical high-pressure pipelines and pressure vessels.
12Cr2MoWVTiB bainitik po'latdan yasalgan yuqori bosimli qozon trubkasi yaxshi keng qamrovli ishlash va yuqori haroratli o'tish qarshiligiga ega va yuqori bosimli qozonlar, ultra yuqori bosimli qozonlar, yuqori haroratli isitgichlar va boshqa sohalar uchun javob beradi. Po'lat quvur yuqori qattiqlik, yuqori quvvat, yaxshi plastika va kuchli emirilish qarshiligiga ega bo'lgan beynit strukturasini qabul qiladi.
12Cr2MoWVTiB yuqori bosimli qozon quvurlariCr, Si va boshqalar kabi oksidlanish qarshiligini yaxshilaydigan elementlar bilan qo'shiladi, shuning uchun ularning maksimal ish harorati 620 darajaga yetishi mumkin. Po'lat quvurlarning tuzilishi va xususiyatlari uzoq muddatli operatsiyadan keyin juda ko'p o'zgarmaydi. Asosan metall harorati 620 darajadan kam yoki unga teng bo'lgan ultra yuqori parametrli qozonlar uchun o'ta isitish quvurlari va isitish quvurlari sifatida ishlatiladi.
GB/T 5610 12Cr2MoWVTiB quvurining kimyoviy tarkibi
| Baho | C | Si | Mn | Cr | Moʻy | V |
| 12Cr2MoWVTib | 0.08-0.15 | 0.45-0.75 | 0.45-0.65 | 1.60-2.10 | 0.50-0.65 | 0.28-0.42 |
| Ti | B | W | P | S | ||
| 0.08-0.18 | 0.002-0.008 | 0.30-0.55 | 0 dan kichik yoki unga teng.025 | 0 dan kichik yoki unga teng.015 |
GB/T 5610 12Cr2MoWVTiB po'lat quvurining mexanik xususiyatlari
| Baho | Kuchlanish kuchi (MPa) | Oqim kuchi (MPa) | Cho'zilish | Qattiqlik |
| 12Cr2MoWVTib | 540-735 | 345 dan katta yoki unga teng | 18% dan katta yoki teng | --- |
12Cr2MoWVTiB qozon trubkasi
12Cr2MoWVTiB qotishma quvurining bir metriga nazariy og'irligi (po'lat zichligi 7,85kg / dm3) hisoblash formulasi:
W=0.02466(D-S)S
Formulada: Vt--Poʻlat quvurning bir metrga nazariy ogʻirligi, kg/m;
D--Poʻlat quvurning nominal tashqi diametri, mm;
S--Poʻlat quvurning nominal devor qalinligi, mm.
yetkazib berish holati
Bu etkazib beriladigan mahsulotning yakuniy plastik deformatsiyasi yoki yakuniy issiqlik bilan ishlov berish holatiga ishora qiladi. Odatda, issiqlik bilan ishlov berishsiz etkazib beriladiganlar issiq haddelenmiş yoki sovuq tortilgan (o'ralgan) holat yoki ishlab chiqarish holati deb ataladi; issiqlik bilan ishlov berishdan so'ng etkazib beriladiganlar issiqlik bilan ishlov berish holati yoki normallashtirilgan (normallashtirilgan), o'chirilgan va qattiqlashtirilgan, qattiq eritma va issiqlik bilan ishlov berish turiga qarab tavlangan deb ataladi. davlat. Buyurtma berishda etkazib berish holati shartnomada ko'rsatilishi kerak.